| CHEMICAL COMPSITION |
RESULTS % Wt. |
| SILICON DIOXIDE (Sio2) |
21.46 |
| ALUMINUM OXIDE (AL2O3) |
4.95 |
| FERRIC OXIDE (Fe2O3) |
3.80 |
| CALCIUM OXIDE (CaO) |
63.36 |
| MAGNESIUM OXIDE (MgO) |
2.00 |
| POTASSIUM OXIDE (K2O) |
0.65 |
| SODIUM OXIDE (Na20) |
0.35 |
| SULFUR TRIOXIDE (SO3) |
2.40 |
| LIME SATUATION FACTOR |
90.10 |
| CHOLORIDES (L.S.F.) |
0.016 |
| LOSS ON IGNITION (I.O.I) |
0.88 |
| FREE LIME (FREE CAO) (F.CAO) |
1.40 |
| TRICALCIUM SILICATE (C3S) |
49.03 |
| DICALCIUM SILCATE (C2S) |
24.55 |
| TRICALCIUM ALUMINATE (C3A) |
6.69 |
| TRICALCIUM ALUMINO FERRICE (C4AF) |
11.56 |
| PHYSICAL POPTES |
RESULS |
| BLAIN |
2900 cm/gr |
| AUTOCLAVE EXPANTION |
0.30 |
| INITIAL SETTING TIME (VICAT) |
130 MINUTES |
| FINAL SETTING TIME (VICAT) |
290 MINTUES |
| COMPRESSIVE STREGTH AT 03 DAYS |
190 kg/cm |
| COMPRESSIVE STREGTH AT 07 DAYS |
310 kg/cm |
| COMPRESSIVE STREGTH AT 28 DAYS |
400 kg/cm |